S-Glass Fiber High Strength
Metallurgy,Chemicals & Energy Composite Materials
MOQ:100 KG
Payment Method : L/C T/T Paypal
Keywords:S-Glass roving S-Glass yarn S-Glass fabric S-Glass fiberglass
| Product Category: | Metallurgy,Chemicals & Energy > Composite Materials | Trademark: | China Beihai |
| Product Package: | carton & pallet | Specifications: | 240，276，400，600，660，735，800，1100，1200，1980，2400 tex |
| Place of Origin: | China | Port: | Shanghai |
S-Glass Fiber high strength
High strength glass fibers made from the magnesium alumino silicate glass system meeting the needs of military application have been developed and put into volume production since 70’ s & 90’ s last century respectively.
Compared with E Glass fiber, they exhibit 30-40% higher tensile strength,16-20% higher modulus of elasticity.10 folds higher fatigue resistance,100-150 degree higher temperature endure, also they have excellent impact resistance because of high elongation to break, high ageing & corrosion resistance, quick resin wet-out properties.
| Feature | |
| ●Good tensile strength. ●High modulus of elasticity ●100 to 150 degrees celsius better temperature endurance ●10 fold higher fatigue resistance ●Excellent impact resistance because of the high elongation to breakage ●High ageing and corrosion resistance ●Quick resin wet-out properties ●Weight saving at the same performance |  |
Application
Aerospace, marine and arms industries due to its high tensile strength and higher modulus of elasticity when compared to e-glass.
Date sheet of S-Glass and E-glass
Data Sheet of S-Glass & E-Glass | ||
Properties | S-Glass | E-Glass |
Virgin Fiber Tensile Strength(Mpa) | 4100 | 3140 |
Tensile Strength(Mpa) ASTM 2343 | 3100-3600 | 1800-2400 |
Tensile Modulus(Gpa) ASTM 2343 | 82-86 | 69-76 |
Elongation To Break(%) | 4.9 | 4.8 |
Properties
Properties | BH-HS2 | BH-HS4 | E-glass |
Virgin fiber tensile strength(Mpa) | 4100 | 4600 | 3140 |
Tensi1e strength(MPA) ASTM2343 | 3100-3600 | 3300-4000 | 1800-2400 |
Tensile Modulus (GPa)ASTM2343 | 82-86 | 83-90 | 69-76 |
Elongation to break(%) | 49 | 54 | 48 |