Main Products:building formworkPP honeycomb
ID:21050651010
Category: Construction & Decoration Building Structural Material
MOQ:300.00 Square Meter(s)
ReusableRecyclableRepairablewaterproofbuilding materialsconstruciton formworkconcrete formworklow costlow density high strengthEasy release
L/CT/T
Product Introduction
The glass fiber reinforced composite building formwork is a three layer sandwich structure, made of MultiTex? and glass fiber reinforced polypropylene composite. The structure is guaranteed in the aspect of material mechanics of the sheet. MultiTex? ensures the strength and impact resistance of the building formwork, thereby greatly improving the service life of the formwork and achieving 200 reusable times. The low density realizes the lightweight of the formwork system, which brings convenience and cost reduction.
The glass fiber reinforced composite building formwork is a thermoplastic composite material, which is unique in its properties makes it particularly suitable for replacing some resource consuming building formwork such as wood formwork in the field of construction.
Specification
1. Standard specification (mm): 1830*915/2440*1220
2. Standard thickness (mm): 10-20.
3. Product color: gray, white.
4. Non-standard specification can be discussed.
Product Advantage
1. Low density, High bending modulus.
2. Waterproof, moisture-proof and non hygroscopic expansion.
3. It is not easy to break and deformation at the corner.
4. Easy release.
5. It can be staples, saws, drills and wrigs as wood.
6. No moldy rot.
7. It is easy to clean and repair.
8. High reusable times.
9. Environmentally friendly recyclable
10. Low cost of single use.
The mechanical properties of Ecollte? building formwork are not comparable to that of general plastic formwork products. The higher bending modulus, the less support need to use, the less likely the formwork will be destroyed, and the economic benefits will be significant.
Technical Data
| Items | Unit | Test Result | |
| Longstar composite formwork | National standard | ||
| Surface hardness | HD | ≥58 | ≥58 |
| Notched impact strength of simply supported beam | KJ/m2 | ≥100 | ≥25 |
| Bending strength | MPa | ≥45 | ≥45 |
| Bending modulus | MPa | ≥4000 | ≥2000 |
| Hot deformation temperature | oC | ≥150 | ≥80 |
| Dimension change rate | % | ≥0.2 | ≥0.2 |
| Mini.temperature of construction | oC | -40~80 | -10 |
| Combustion performance rating | level | satisfy | ≥E |
Comparison
| Item | Composite building formwork | Plywood | Steel formwork | Aluminum formwork |
| Density | 0.6 g/cm3 - 0.9 g/cm3 | 0.8 g/cm3 | 7.85 g/cm3 | 2.8 g/cm3 |
| Antisepsis and mildew resistance | Decay resistant and mildew free | Rot and mildew | Rust | Decay resistant and mildew free |
| Scratch resistance | excellent | Depends on the thickness of the film. | excellent | excellent |
| Impact resistance | excellent | commonly | Deformation after impact | Deformation after impact |
| Saw, nail, twist | Easy | Easy | can not | can not |
| Repairability | Easy repair | Non repairable | Repairable | Repairable |
| Clear | Easy to clean up | Easy to clean up | not easy to clean up. | not easy to clean up. |
| Expected service life | More than 200 times | 3-10 times | More than 100 times | More than 300 times |
| construction | convenient | Soybean wood fixation is needed. | Need large scale crane hoisting. | Need large scale city hoisting |
| Salvage value | Normal | Extremely low | high | high |
| average cost | Very low | high | low | low |
| Performance changes after moisture absorption | unchanged | Expansion and performance degradation | No change | No change |